SIMFIT RESULTS
==============

Dataset : C:\BRUKER\TopSpin4.0.6\data\NMR\AVIII/bd99165.4mmHXY.08042022.29Si.Li6.75P0.25Si0.75O5Cl/1/pdata/991/ct1t2.txt

INTENSITY fit : Exponential decay (T2 or T1rho) : I[t]=I[0]*exp(-t/T)

60 points for Peak 1

Converged after 315 iterations!

Results     Comp. 1       Comp. 2    

I[0]  =    3.346e+00    -2.320e+00  
T     =      64.927s       89.596s  

RSS   =    8.921e-03
SD    =    1.219e-02

Point       Tau          Expt          Calc       Difference

    1       1.000s     1.000e+00     1.002e+00    1.545e-03
    2       2.000s     9.762e-01     9.766e-01    4.431e-04
    3       3.000s     9.522e-01     9.522e-01    5.898e-05
    4       4.000s     9.280e-01     9.283e-01    2.291e-04
    5       5.000s     9.040e-01     9.048e-01    7.965e-04
    6       6.000s     8.802e-01     8.818e-01    1.614e-03
    7       7.000s     8.567e-01     8.592e-01    2.546e-03
    8       8.000s     8.337e-01     8.371e-01    3.472e-03
    9       9.000s     8.112e-01     8.155e-01    4.288e-03
   10      10.000s     7.893e-01     7.942e-01    4.909e-03
   11      11.000s     7.681e-01     7.734e-01    5.268e-03
   12      12.000s     7.477e-01     7.530e-01    5.317e-03
   13      13.000s     7.280e-01     7.330e-01    5.029e-03
   14      14.000s     7.090e-01     7.134e-01    4.398e-03
   15      15.000s     6.908e-01     6.942e-01    3.432e-03
   16      16.000s     6.732e-01     6.754e-01    2.159e-03
   17      17.000s     6.563e-01     6.569e-01    6.214e-04
   18      18.000s     6.400e-01     6.389e-01   -1.126e-03
   19      19.000s     6.242e-01     6.211e-01   -3.018e-03
   20      20.000s     6.088e-01     6.038e-01   -4.982e-03
   21      21.000s     5.938e-01     5.868e-01   -6.941e-03
   22      22.000s     5.790e-01     5.702e-01   -8.815e-03
   23      23.000s     5.644e-01     5.539e-01   -1.053e-02
   24      24.000s     5.499e-01     5.379e-01   -1.201e-02
   25      25.000s     5.354e-01     5.222e-01   -1.318e-02
   26      26.000s     5.209e-01     5.069e-01   -1.400e-02
   27      27.000s     5.063e-01     4.919e-01   -1.442e-02
   28      28.000s     4.916e-01     4.772e-01   -1.440e-02
   29      29.000s     4.767e-01     4.628e-01   -1.392e-02
   30      30.000s     4.617e-01     4.487e-01   -1.298e-02
   31      31.000s     4.465e-01     4.349e-01   -1.159e-02
   32      32.000s     4.312e-01     4.214e-01   -9.787e-03
   33      33.000s     4.158e-01     4.082e-01   -7.600e-03
   34      34.000s     4.003e-01     3.952e-01   -5.087e-03
   35      35.000s     3.848e-01     3.825e-01   -2.315e-03
   36      36.000s     3.695e-01     3.701e-01    6.380e-04
   37      37.000s     3.543e-01     3.580e-01    3.689e-03
   38      38.000s     3.393e-01     3.461e-01    6.747e-03
   39      39.000s     3.247e-01     3.344e-01    9.719e-03
   40      40.000s     3.105e-01     3.230e-01    1.251e-02
   41      41.000s     2.968e-01     3.119e-01    1.503e-02
   42      42.000s     2.838e-01     3.010e-01    1.720e-02
   43      43.000s     2.714e-01     2.903e-01    1.893e-02
   44      44.000s     2.597e-01     2.799e-01    2.016e-02
   45      45.000s     2.488e-01     2.696e-01    2.082e-02
   46      46.000s     2.388e-01     2.596e-01    2.087e-02
   47      47.000s     2.296e-01     2.499e-01    2.029e-02
   48      48.000s     2.213e-01     2.403e-01    1.905e-02
   49      49.000s     2.138e-01     2.309e-01    1.715e-02
   50      50.000s     2.072e-01     2.218e-01    1.462e-02
   51      51.000s     2.014e-01     2.129e-01    1.147e-02
   52      52.000s     1.963e-01     2.041e-01    7.758e-03
   53      53.000s     1.920e-01     1.956e-01    3.537e-03
   54      54.000s     1.883e-01     1.872e-01   -1.126e-03
   55      55.000s     1.852e-01     1.790e-01   -6.155e-03
   56      56.000s     1.825e-01     1.710e-01   -1.147e-02
   57      57.000s     1.802e-01     1.632e-01   -1.697e-02
   58      58.000s     1.782e-01     1.556e-01   -2.258e-02
   59      59.000s     1.763e-01     1.481e-01   -2.819e-02
   60      60.000s     1.746e-01     1.408e-01   -3.374e-02

============================================================